CHARACTERISTICS AND APPLICATION:
- Camel CM185 submerged arc welding is manufactured using OERLIKON technology on a modern and stable production line.
- CM185 is Aluminate-Rutile cure. In the welding process outside the function of covering the weld protection, the welding drug also added a suitable amount of Silicon and Manganese to improve the welding properties.
- CM185 welding capsule produces less slag, reducing wear and tear. DC or AC current can be welded and allow for high speed welding, good weld shape, stable arc and slag.
- CM185 welding drug is heated to 850 ° C so that the molten water is thoroughly deacidified to ensure that the welds are not porous. The residual hydrocarbon content in the low weld results in high weld strength.
PACKAGING SPECIFICATION:
Net weight of packing (Kg) |
25 |
MECHANICAL PROPERTIES OF WELD:
Type of welding wire | Strength limit (Mpa) | Yield limit (MPa) | Elongation (%) | Pendulum impact ( J ) |
EL12 (F6A2) | 420 ( min ) | 330 (min) | 22 (min ) | 53 (min)/-18OC |
EM12K (F7A2) | 500 (min) | 410 (min) | 22 (min ) | 45 (min)/-20OC |
CHEMICAL COMPOSITION OF WELDING METAL LAYER (%):
Type of welding wire | C | Si | Mn |
EM12K | 0.05-0.10 | 0.05-01.0 | 1.4-1.6 |
Graininess: from 14 ~ 60mechs, equivalent to 0.3mm ~ 2.5mm
NOTE:
- When welding capsule is moist, welding smoked, splashed and unstable, difficult to remove the powder should be dried before the welding.
- Keeping the welding capsule in dry places, wrapped in dusty, damp packaging, avoid tearing the package of welding capsule.
- Always maintaining the right amount of protection under the guidance to get deep weld, high work ability.